铝板在染色时影响其质量的因素有哪些呢?

来源:  发布时间:2020-10-21 17:19:09  

关于铝板在染色时影响其质量的因素有哪些呢?大家一起来了解一下;
What factors affect the quality of aluminum plate in dyeing? Let's have a look;
氧化膜对于铝板的质量有很大的影响。氧化膜就是指铝板在生产的过程中的厚度、孔隙率、透明度等。铝板中膜层的厚度保持在10um以上就可以了,孔隙率以及透明度,这样就可以得到比较好的染色质量。
The oxide film has a great influence on the quality of aluminum plate. Oxide film refers to the thickness, porosity and transparency of aluminum plate in the production process. The thickness of the film in the aluminum plate should be kept above 10um. The porosity and transparency of the film can make the dyeing quality better.
染色的温度
Dyeing temperature
铝板在染色的过程中分为冷染与热染。使用冷染,所耗费的时间比较长,在染色的过程中期色彩的均匀性比较好掌握。热染使用时间比较短,但是在染色的过程中对于颜色的操控比较难。热染的温度通常在10-60℃。如果在染色的过程中,温度过高,会减小染色的吸附性,并且容易导致铝板表面发花。
Aluminum plate can be divided into cold dyeing and hot dyeing. It takes a long time to use cold dyeing, and the uniformity of color is easy to master in the middle of dyeing process. The use time of hot dyeing is relatively short, but it is difficult to control the color in the dyeing process. The temperature of hot dyeing is usually 10-60 ℃. If the temperature is too high in the process of dyeing, the adsorption of dyeing will be reduced, and the surface of aluminum plate will be easy to flower.

 

铝板生产厂家
铝板制件原料的影响
Influence of raw materials on aluminum plate parts
通常大家在生产的过程中高纯铝、铝镁、铝锰合金经过阳极氧化以后,其中染色的功能是最好的,可以染成各种各样的颜色。对于含有硅或铜比较重的板材,在染色的过程中只能够染成深色与黑色,比较单调的颜色。
Generally, after anodizing of high purity aluminum, aluminum magnesium and aluminum manganese alloy, the dyeing function is the best and can be dyed into various colors. For the heavy plate containing silicon or copper, only dark and black colors can be dyed in the dyeing process.
染色液浓度
Dye concentration
铝板的浓度与染色之间存在一定的联系,如果铝板染成淡色,其中浓度可以降低一点,染成深色浓度可以高一点。
There is a certain relationship between the concentration of aluminum plate and dyeing. If the aluminum plate is dyed in light color, the concentration can be reduced a little, and the dark color can be higher.
通常所生产的铝板材料所染比较淡的颜色其色彩为0.1-0.39g/L,染淡色彩为1g/L,染深色彩为3-5g/L,染稠密的色彩为10-15g/L,如果要求的染色浓度比较高就会造成颜色不均或者会出现浮色的现象,在清洁与关闭的过程汇总容易产生流色。
Generally, the light color of aluminum plate material is 0.1-0.39g/l, light color is 1g / L, deep color is 3-5g / L, and dense color is 10-15g / L. if the required dyeing concentration is relatively high, it will cause uneven color or floating color phenomenon, which is easy to produce color flow in the process of cleaning and closing.
为了加强其染色的吸附性能,这样可以使用低浓度颜色进行延伸染色,这样可以使染料能够比较均匀的渗透到氧化膜中,这样可以使染色更加和谐与牢固。
In order to strengthen the adsorption property of the dye, low concentration color can be used for extended dyeing, which can make the dye more evenly penetrate into the oxide film, which can make the dyeing more harmonious and firm.